PECVD1 Recipes: Difference between revisions
Jump to navigation
Jump to search
| Line 15: | Line 15: | ||
== SiO<sub>2</sub> deposition (PECVD #1) == |
== SiO<sub>2</sub> deposition (PECVD #1) == |
||
*[[media:PECVD1-SiO2-standard recipe 2014.pdf|SiO<sub>2</sub> Standard Recipe]] |
*[[media:PECVD1-SiO2-standard recipe 2014.pdf|SiO<sub>2</sub> Standard Recipe]] |
||
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dEw0bjFEdTF2SUhRa25Ca0d0SzBha3c&usp=drive_web#gid=sharing SiO<sub>2</sub> Data |
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dEw0bjFEdTF2SUhRa25Ca0d0SzBha3c&usp=drive_web#gid=sharing SiO<sub>2</sub> Data December 2014] |
||
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dDQ3VEtZQVRpdVdlbGtIZHpTNmFzNmc&usp=sharing SiO<sub>2</sub> 1000A Thickness uniformity 2014] |
*[https://docs.google.com/spreadsheet/ccc?key=0AnwBU1s4JQo2dDQ3VEtZQVRpdVdlbGtIZHpTNmFzNmc&usp=sharing SiO<sub>2</sub> 1000A Thickness uniformity 2014] |
||
Revision as of 23:42, 3 December 2014
PECVD 1 (PlasmaTherm 790)
SiN deposition (PECVD #1)
- SiN Standard Recipe
- SiN Data December 2014
- SiN 1000A Thickness uniformity 2014
- Low Stress Si3N4 - Variable Stress Recipes
- Low Stress Si3N4 - Variable Stress Plot
- Deposition rate~11.23nm/min (users must calibrate this prior to critical deps)
- HF e.r.~89nm/min
- Stress~450MPa
- Refractive Index~1.942
SiO2 deposition (PECVD #1)
- Deposition rate~35.52nm/min (users must calibrate this prior to critical deps)
- HF e.r.~645nm/min
- Stress~-408MPa
- Refractive Index~1.461
SiOxNy deposition (PECVD #1)
- SiOxNy Deposition Recipes - Varying N/O Ratio
- SiOxNy Stress/Index vs. O/N Ratio
- SiOxNy Recipe
- SiOxNy Data November 2014
- SiOxNy 3000A Thickness uniformity 2014
- Deposition rate~14.99nm/min (users must calibrate this prior to critical deps)
- HF e.r.~417nm/min
- Stress~133MPa
- Refractive Index~1.714