About
Materials Table
Materials Table
| ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Material | Symbol | Density, g/cm3 | Z Ratio | Tooling, % | Comments | |||||||
| Aluminum | Al | 2.70 | 1.08 | Antimony | Sb | 2.70 | 0.768 | |||||
| Arsenic | As | 5.73 | 0.996 | |||||||||
| Beryllium | Be | 1.85 | 0.543 | |||||||||
| Boron | B | 2.54 | 0.389 | |||||||||
| Cadmium | Cd | 8.64 | 0.682 | |||||||||
| Cadmium sulfide | CdS | 4.83 | 1.02 | |||||||||
| Cadmium telluride | CdTe | 5.85 | 0.980 | |||||||||
| Calcium fluoride | CaF2 | 3.18 | 0.775 | |||||||||
| Carbon (graphite) | C | 2.25 | 3.26 | |||||||||
| Chromium | Cr | 7.20 | 0.305 | 155 | ||||||||
| Cobalt | Co | 8.71 | 0.343 | |||||||||
| Copper | Cu | 8.93 | 0.437 | |||||||||
| Gallium | Ga | 5.93 | 0.593 | |||||||||
| Gallium Arsenide | GaAs | 5.31 | 1.59 | |||||||||
| Germanium | Ge | 5.35 | 0.516 | |||||||||
| Gold | Au | 19.30 | 0.381 | |||||||||
| Indium | In | 7.30 | 0.841 | 120 | ||||||||
| Indium antimonide | InSb | 5.76 | 0.769 | |||||||||
| Iridium | Ir | 22.4 | 0.129 | |||||||||
| Iron | Fe | 7.86 | 0.349 | |||||||||
| Lead | Pb | 11.3 | 1.13 | |||||||||
| Lead sulfide | PbS | 7.50 | 0.566 | |||||||||
| Lithium fluoride | LiF | 2.64 | 0.774 | |||||||||
| Magnesium | Mg | 1.74 | 1.61 | |||||||||
| Magnesium oxide | MgO | 3.58 | 0.411 | |||||||||
| Magnesium Fluoride | MgF2 | 3.00 | 0.427 | |||||||||
| Manganese | Mn | 7.20 | 0.377 | |||||||||
| Manganese(II) Sulfide | MnS | 3.99 | 0.94 | |||||||||
| Mercury | Hg | 13.46 | 0.74 | |||||||||
| Molybdenum | Mo | 10.2 | 0.257 | |||||||||
| Nickel | Ni | 8.91 | 0.331 | |||||||||
| Niobium | Nb | 8.57 | 0.493 | |||||||||
| Niobium(V) Oxide | Nb2O5 | 4.47 | ||||||||||
| Palladium | Pd | 12.0 | 0.357 | |||||||||
| Platinum | Pt | 21.4 | 0.245 | |||||||||
| Potasium Cloride | KCl | 1.98 | 2.05 | |||||||||
| Selenium | Se | 4.82 | 0.864 | |||||||||
| Silicon | Si | 2.32 | 0.712 | |||||||||
| Silicon(II) Oxide | SiO | 2.13 | 0.87 | |||||||||
| Silicon dioxide (fused quarz) | SiO2 | 2.20 | 1.07 | |||||||||
| Silver | Ag | 10.5 | 0.529 | |||||||||
| Silver bromide | AgBr | 6.47 | 1.18 | |||||||||
| Silver chloride | AgCl | 5.56 | 1.32 | |||||||||
| Sodium | Na | 0.97 | 4.8 | |||||||||
| Sodium chloride | NaCl | 2.17 | 1.57 | |||||||||
| Tantalum | Ta | 16.6 | 0.262 | |||||||||
| Tantalum(IV) oxide | Ta2O5 | 8.2 | 0.30 | |||||||||
| Tin | Sn | 7.30 | 0.724 | |||||||||
| Titanium | Ti | 4.50 | 0.628 | |||||||||
| Titanium (IV) Oxide | TiO2 | 4.26 | 0.40 | |||||||||
| Titanium Oxide | TiO | 4.90 | N/A | |||||||||
| Tangsten | W | 19.3 | 0.163 | |||||||||
| Tangsten carbide | WC | 15.6 | 0.151 | |||||||||
| Zinc | Zn | 7.04 | 0.514 | |||||||||
| Zinc Oxide | Zn | 5.61 | 0.556 | |||||||||
| Zinc Sulfide | ZnS | 4.09 | 0.775 | |||||||||
| Zirconium | Zr | 6.51 | 0.60 | |||||||||
| Zirconium Oxide | ZrO2 | 5.6 | ||||||||||