RIE 5 (PlasmaTherm)

RIE 5 (PlasmaTherm) Location Bay 2 Tool Type Dry Etch Manufacturer Plasmatherm (Unaxis) Model SLT 770 Description RIE #5 Programmable, Loadlocked Chlorine-Based System Primary Supervisor Aidan Hopkins (805) 893-2343 hopkins@ece.ucsb.edu Secondary Supervisor Bill Millerski Recipes Dry Etch Recipes SignupMonkey: Sign up for this tool

About

This computer-controlled, turbo-pumped RIE is the "work horse" of the processing laboratory due to it's ease of operation and versatility. It can be operated manually or in a fully programmable mode from sample loading to etching to sample unloading. Samples are placed on a silicon carrier with or without a bonding agent to facilitate sample cooling. Etching is done with oxygen or chlorine-based gases @ 13.56 Mhz. Oxygen is used for etching of photoresists and polyimide. Chlorine-based gases are used for etching semiconductors and some metals. Typical semiconductor materials that are etched are: AlGaAs, InGaAs, AlGaSb, GaN, and Si. Metals that can be etched include Al, Ti, and Cr layers. Good masking materials for the chlorine-based etching are photoresist (at powers < 200 W), Ni, SiO₂, and SrF₂. The wafer chuck can be heated to 80°C through liquid-based heating. This makes etching of high In-containing compounds difficult due to the non-volatility of In-chlorides. A high physical component (Ar in the mixture) is required for etching of InP and the surface will be contaminated with residual etch products when finished.

Special features include: a true sample loadlock, substrate backside helium cooling, heating up to 80°C, four inch sample holder, HeNe laser etch monitor and chart recorder. Various devices that use this tool as an integral processing step include: in-plane lasers, VCSELs, micro-lenses, Bragg-Fresnel lens, FETs, HBTs, etc.

Detailed Specifications

• Etch gases include: Cl₂, BCl₃, SiCl₄, O₂, Ar
• Full computer control or manual computer control
• Low 1 E-7 ultimate chamber pressure
• 13.56 Mhz excitation frequency
• Sample chuck He-backside cooled / heated (up to 80°C)
• Laser Etch monitor: large spot size, no camera/alignment method.
  • Requires full ~1cm witness sample/area in center of wafer.

Documentation

• RIE#5: Standard Operating Procedure (Cortex Software)
• How to restart the software on RIE #5

Recipes

You can find dry etch recipes on Recipes > Dry Etch > RIE5 Recipes

Typical etch conditions for GaAs:

• 10 mT (15 sccm BCl₃ / 10 sccm SiCl₄)
• 100 W, constant power
• 60 nm / min. etch rate