Difference between revisions of "Thermal Evaporation Recipes"
Jump to navigation
Jump to search
Line 217: | Line 217: | ||
=[[Thermal Evaporator 2]]= |
=[[Thermal Evaporator 2]]= |
||
− | = Materials Table = |
||
− | |||
− | {| border="1" style="border: 1px solid #D0E7FF; background-color:#ffffff; text-align:center; font-size: 95%" class="collapsible collapsed wikitable" |
||
− | |- |
||
− | ! colspan=6 width=1300 height=35 bgcolor="#D0E7FF" align="center"|<div style="font-size: 150%;">Materials Table</div> |
||
− | |- bgcolor="#D0E7FF" |
||
− | ! width="45" bgcolor="#D0E7FF" align="center" | '''Material''' |
||
− | ! width="45" bgcolor="#D0E7FF" align="center" | '''Symbol''' |
||
− | ! width="45" bgcolor="#D0E7FF" align="center" | '''Density, g/cm3''' |
||
− | ! width="45" bgcolor="#D0E7FF" align="center" | '''Z Ratio''' |
||
− | ! width="45" bgcolor="#D0E7FF" align="center" | '''Tooling, %''' |
||
− | ! width="100" bgcolor="#D0E7FF" align="center" | '''Comments''' |
||
− | |- |
||
− | |Aluminum |
||
− | |Al |
||
− | |2.70 |
||
− | |1.08 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Antimony |
||
− | |Sb |
||
− | |6.620 |
||
− | |0.768 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Arsenic |
||
− | |As |
||
− | |5.73 |
||
− | |0.996 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Beryllium |
||
− | |Be |
||
− | |1.85 |
||
− | |0.543 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Boron |
||
− | |B |
||
− | |2.54 |
||
− | |0.389 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Cadmium |
||
− | |Cd |
||
− | |8.64 |
||
− | |0.682 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Cadmium sulfide |
||
− | |CdS |
||
− | |4.83 |
||
− | |1.02 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Cadmium telluride |
||
− | |CdTe |
||
− | |5.85 |
||
− | |0.980 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Calcium fluoride |
||
− | |CaF<sub>2</sub> |
||
− | |3.18 |
||
− | |0.775 |
||
− | | |
||
− | |Used often |
||
− | |- |
||
− | |Carbon (graphite) |
||
− | |C |
||
− | |2.25 |
||
− | |3.26 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Chromium |
||
− | |Cr |
||
− | |7.20 |
||
− | |0.305 |
||
− | |155 |
||
− | |Used often |
||
− | |- |
||
− | |Cobalt |
||
− | |Co |
||
− | |8.71 |
||
− | |0.343 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Copper |
||
− | |Cu |
||
− | |8.93 |
||
− | |0.437 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Gallium |
||
− | |Ga |
||
− | |5.93 |
||
− | |0.593 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Gallium Arsenide |
||
− | |GaAs |
||
− | |5.31 |
||
− | |1.59 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Germanium |
||
− | |Ge |
||
− | |5.35 |
||
− | |0.516 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Gold |
||
− | |Au |
||
− | |19.30 |
||
− | |0.381 |
||
− | | |
||
− | |Used often |
||
− | |- |
||
− | |Indium |
||
− | |In |
||
− | |7.30 |
||
− | |0.841 |
||
− | |120 |
||
− | |Used often |
||
− | |- |
||
− | |Indium antimonide |
||
− | |InSb |
||
− | |5.76 |
||
− | |0.769 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Iridium |
||
− | |Ir |
||
− | |22.4 |
||
− | |0.129 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Iron |
||
− | |Fe |
||
− | |7.86 |
||
− | |0.349 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Lead |
||
− | |Pb |
||
− | |11.3 |
||
− | |1.13 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Lead sulfide |
||
− | |PbS |
||
− | |7.50 |
||
− | |0.566 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Lithium fluoride |
||
− | |LiF |
||
− | |2.638 |
||
− | |0.778 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Magnesium |
||
− | |Mg |
||
− | |1.74 |
||
− | |1.61 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Magnesium oxide |
||
− | |MgO |
||
− | |3.58 |
||
− | |0.411 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Magnesium Fluoride |
||
− | |MgF<sub>2</sub> |
||
− | |3.00 ( should be 3.18) |
||
− | |0.427( should be 0.637) |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Manganese |
||
− | |Mn |
||
− | |7.20 |
||
− | |0.377 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Manganese(II) Sulfide |
||
− | |MnS |
||
− | |3.99 |
||
− | |0.94 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Mercury |
||
− | |Hg |
||
− | |13.46 |
||
− | |0.74 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Molybdenum |
||
− | |Mo |
||
− | |10.2 |
||
− | |0.257 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Nickel |
||
− | |Ni |
||
− | |8.91 |
||
− | |0.331 |
||
− | | |
||
− | |Used often |
||
− | |- |
||
− | |Niobium |
||
− | |Nb |
||
− | |8.578 |
||
− | |0.492 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Niobium(V) Oxide |
||
− | |Nb<sub>2</sub>O<sub>5</sub> |
||
− | |4.47 |
||
− | |*1.00 |
||
− | | |
||
− | |*z ratio has not been established |
||
− | |- |
||
− | |Palladium |
||
− | |Pd |
||
− | |12.0 |
||
− | |0.357 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Platinum |
||
− | |Pt |
||
− | |21.4 |
||
− | |0.245 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Potasium Cloride |
||
− | |KCl |
||
− | |1.98 |
||
− | |2.05 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Selenium |
||
− | |Se |
||
− | |4.82 |
||
− | |0.864 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Silicon |
||
− | |Si |
||
− | |2.32 |
||
− | |0.712 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Silicon(II) Oxide |
||
− | |SiO |
||
− | |2.13 |
||
− | |0.87 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Silicon dioxide (fused quarz) |
||
− | |SiO<sub>2</sub> |
||
− | |2.20 |
||
− | |1.07 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Silver |
||
− | |Ag |
||
− | |10.5 |
||
− | |0.529 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Silver bromide |
||
− | |AgBr |
||
− | |6.47 |
||
− | |1.18 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Silver chloride |
||
− | |AgCl |
||
− | |5.56 |
||
− | |1.32 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Sodium |
||
− | |Na |
||
− | |0.97 |
||
− | |4.8 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Sodium chloride |
||
− | |NaCl |
||
− | |2.17 |
||
− | |1.57 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Tantalum |
||
− | |Ta |
||
− | |16.6 |
||
− | |0.262 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Tantalum(IV) oxide |
||
− | |Ta<sub>2</sub>O<sub>5</sub> |
||
− | |8.2 |
||
− | |0.30 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Tin |
||
− | |Sn |
||
− | |7.30 |
||
− | |0.724 |
||
− | | |
||
− | |Used often |
||
− | |- |
||
− | |Titanium |
||
− | |Ti |
||
− | |4.50 |
||
− | |0.628 |
||
− | | |
||
− | |Used often |
||
− | |- |
||
− | |Titanium (IV) Oxide |
||
− | |TiO<sub>2</sub> |
||
− | |4.26 |
||
− | |0.40 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Titanium Oxide |
||
− | |TiO |
||
− | |4.90 |
||
− | |*1.00 |
||
− | | |
||
− | |* z ratio not established |
||
− | |- |
||
− | |Tungsten |
||
− | |W |
||
− | |19.3 |
||
− | |0.163 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Tungsten carbide |
||
− | |WC |
||
− | |15.6 |
||
− | |0.151 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Zinc |
||
− | |Zn |
||
− | |7.04 |
||
− | |0.514 |
||
− | | |
||
− | |Used often |
||
− | |- |
||
− | |Zinc Oxide |
||
− | |ZnO |
||
− | |5.61 |
||
− | |0.556 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Zinc Sulfide |
||
− | |ZnS |
||
− | |4.09 |
||
− | |0.775 |
||
− | | |
||
− | | |
||
− | |- |
||
− | |Zirconium |
||
− | |Zr |
||
− | |6.51 |
||
− | |0.60 |
||
− | | |
||
− | |Should be 6.49 |
||
− | |- |
||
− | |Zirconium Oxide |
||
− | |ZrO<sub>2</sub> |
||
− | |5.6 |
||
− | |1.001 |
||
− | | |
||
− | | |
||
− | |- |
Revision as of 14:25, 31 March 2014
Back to Vacuum Deposition Recipes.
Thermal Evaporator 1
Materials Table
Thermal Evaporator 2
Materials Table
| |||||||
---|---|---|---|---|---|---|---|
Material | Symbol | Density, g/cm3 | Z Ratio | Tooling, % | Current, Amp | Dep.rate, A/sec | Comments |
Aluminum | Al | 2.70 | 8.17 | 95 | 85 | 1 | Used often |
Chromium | Cr | 7.20 | 28.95 | 95 | 85 | 2 | Used often |
Cobalt | Co | 8.71 | 25.74 | ||||
Copper | Cu | 8.93 | 20.21 | 100 | Used often | ||
Gold | Au | 19.32 | 23.18 | 101.2 | 122 | 5 | Used often |
Gold/Palladium | Au.5/Pd.5 | 15.86 | 23.96 | ||||
Gold/Palladium | Au.5/Pd.4 | 16.40 | 23.80 | ||||
Gold/Zinc | Au.95/Zn.05 | 18.72 | 22.89 | 101.2 | |||
Gold/Zinc | Au.90/Zn.10 | 18.07 | 22.58 | ||||
Magnezium | Mg | 1.74 | 5.48 | 98.4 | |||
Manganese | Mn | 7.20 | 23.40 | 120 | 100 | ||
Nickel | Ni | 8.90 | 26.68 | 100 | 50 | 4.5 | Used often |
Nichrome | NiCr | 8.32 | 27.59 | 100 | 0.4 | ||
Palladium | Pd | 12.40 | 24.73 | 140.5 | 62 | 1.5 | Used often |
Silicon Monoxide | SiO | 2.13 | 10.19 | 120 | 70 | ||
Silver | Ag | 10.5 | 16.69 | ||||
Zinc | Zn | 7.14 | 17.18 | 50 | 4.5 | Used often | |
Zinc Oxide | ZnO | 5.61 | 15.88 | ||||
StrontiumFluoride | SrF2 | 4.28 | 12.15 | 200 | |||
Iron | Fe | 7.86 | 25.30 | ||||
ITO(IndiumTinOxide) | In2O3 - SnO2 | 6.43-7.14 | 0.841 | ||||
Permalloy | Ni0.1Fe0.2 | 8.7 | 26.40 | 140 | 0.1 |