SEM 1 (JEOL IT800SHL)
| ||||||||||||||||||||||||||
About
The JEOL IT800HSL Field Emission Scanning Electron Microscope is used for imaging a variety of samples made in the facility.
Capabilities
The system has multiple detectors, detailed below. Low-vacuum mode reduces sample charging by introducing N2 gas into the chamber, without sacrificing imaging quality (using a special vacuum nozzle on the electron column). Our system is equipped with a gentle-beam mode of operation where bias is put on the stage, allowing for high resolution imaging at low electron energies impinging the surface. Both of these are useful for imaging low conductivity and insulating materials without the need for conductive layer coatings.
The system can accept a 6” wafer, but only XYZXYZ mm of the wafer is accessible with the stage movement.
The Hummer coater is used to deposit a thin AuPd on your samples, to reduce electrical charging of insulating samples (such as SiO2 substrates, or thick >1µm layers of SiO2 or PR).
This SEM also has an Electron-Beam Lithography Nabity system. Contact the supervisor for info.
Detailed Specifications
Imaging
- Resolution:
- 0.5nm at 15kV SHL mode
- 0.7nm at 1kV
- 0.9nm at 500V
- Magnification:
- Photo magnification: x10 to x2,000,000 (128mm x 96mm)
- Display magnification: x27 to x5,480,000 (1280pix x 960pix)
- Imaging Modes:
- STD: Standard
- LDF: Large depth of focus
- BD: Beam deceleration
- Applies negative voltage to sample stage to increase effective acceleration without increasing beam acceleration (reducing charging).
- SHL: Super hybrid lens
- Detectors
- SED: Secondary electron detector (low angle)
- UHD: Ultra high resolution detector
- SBED: Scintillated back scatter electron detector
- Inserts between the objective lens and the sample
- LVBED: Low vacuum back scatter electron detector
- LVSED: Low vacuum secondary electron detector
- Accelerating Voltages:
- SEM: 0.01 to 30kV
- Probe currents
- A few pA to 500nA (30kV) 100nA (5kV)
- Specimen stage
- X: 140mm Y: 80mm
- Z: 6mm to 41mm
- Tilt: -5 to 70 degrees (depending on sample holder and offset)
- Rotation: 360 degrees
Mechanical
- Max Sample Size: 6-inch wafer
- Stage movement:
- max: 70 x 50mm
- 4-inch wafer: limited to ~25x25mm movement area from wafer center.
- Tilt: -5° to varies. Tilt is dependent on sample holder, stage height, and offset value.
- Rotation: 360°
- Specimen holders :
- Copper and XYZ Carbon tape available
- 4-inch wafer with topside clips
- 1-inch holder for 30°/90°, 45°/90° mounting with tape or clips.
Operating Procedures
- JEOL IT800SHL Operating Procedure.
- Optimizing Astigmatism (CalTech Nanoscience Institute)
- Stig is the most common cause of blurry images.
- A Common mistake is to optimize stig on flat lines (eg. a cleaved edge or line/space features). This always leads to accidentally skewing the stig in the direction of the lines. Instead, make sure to optimize on a roundish feature, such as a piece of dust/debris.