Thermal Processing Recipes

Tystar 8300

Thermal Oxidation of Silicon - Calculating Oxidation Times

Online calculators for thermal oxidation can be used to estimate the oxidation time for a desired oxidation thickness. Please see the Calculators + Utilities page for links to these oxidation calculators.

Using the Stanford Leland Jr. "Advanced Silicon Thermal Oxide Thickness Calculator", we have determined the following simulation parameters to predict oxidation times. Pleas enote, however, that doping level, impurity concentration and other factors can alter these calibrations, so you may need to calibrate the Partial Pressure yourself if you need higher accuracy.

Thermal Oxidation Recipes

1050°C Dry Oxidation

• Recipe Name: DRY1050
• Tube #2 for Cleaned Silicon Only
• Tube #3 for processed silicon or other anneals.

Simulation Parameters

• Partial Pressure = 1.12
• <100>, 1050°C, 10Å Native Oxide, no dopants

Measurements and Curve-Fitting for 1050°C Dry oxidations. Note: three data points only.

1050°C Wet Oxidation

• Recipe Name: WET1050
• Tube #2 for Cleaned Silicon Only
• Tube #3 for processed silicon or other anneals.

Simulation Parameters

• Partial Pressure = 1.09
• <100>, 1050°C, 10Å Native Oxide, no dopants

Measurements and Curve-Fitting for 1050°C Wet oxidations.	Zoom-in on Measurements and Curve-Fitting for 1050°C Wet oxidations.

AlGaAs Oxidation

A recipe is available on Tube #1 for thermal oxidation of AlGaAs layers, at much lower temperatures than Tubes #2 & #3. There are special procedures for running this lower-temp. oxidation at shorter times, please contact Tony Bosch or the NanoFab process Group for more information.

Wafer Substrate Bonding

Direct Bonding

Numerous research groups perform direct wafer bonding (of various materials) using either the Suss Wafer Bonder, or a custom graphite fixture in conjunction with any one of numerous ovens, such as the N2-purged Wafer Bonding Furnace (with glove box) or N2-purged Blue M oven.

Il addition, the Fine-Tech Flip-Chip Bonder can perform aligned bonding of various-sized pieces.

The EVG Plasma Activation system and Goniometer allow for surface prep/inspection prior to bonding.

Bonding with Intermediate layer

The Logitech Bonder allows wafer-bonding with a CrystalBond wax intermediate layer. Please see Don Freeborn for recipes.

Tube Furnace AlGaAs Oxidation (Lindberg)

Oxidation of AlGaAs (high-Aluminum content >90%) is performed in this furnace, at temperatures between 200°C → 500°C.

Maximum time is about 3 hours before the bubble water temperature becomes uncontrolled.

Recipes are available, please ask the NanoFab Process group staff.

Rapid Thermal Processor (SSI Solaris 150)

To Do: Add starting recipes for RTP